MIL RFマイクロ波多層セラミックチップコンデンサMLCC CCDA
●低損失の特性があります, 高い電力容量の安定性と高い信頼性;
●高周波回路のあらゆる種類の機器に適しています, amplification circuit
Temperature coefficient: NPO法人: 0 ± 30ppm /℃
Capacitance drift: no more than ± 2% or ± 0.05 pF, take the larger
Loss angle tangent: not exceeding 15% at a frequency of 1 MHz / 1 KHz
絶縁抵抗 (25℃): 100000M Ω
Medium voltage resistance (test surge current does not exceed 50mA): 5 UR
動作温度: -55~125℃
| divide into groups | inspecting item | Requires the chapter number | Test method chapter number | sampling plan |
| A divide into groups | Voltage treatment | 3.8 in ZZR-Q / CT 20003-2018 | 4.5.3 in GJB 192B- 2011 | 100% |
|
A divide into groups |
絶縁抵抗 (125℃) |
3.11 in ZZR-Q / CT 20003- 2018 |
4.5.6 in GJB 192B- 2011 |
In accordance with GJB 192B-2011
テーブル 6 |
|
A divide into groups |
Visual and mechanical inspection | 3.3 in ZZR-Q / CT 20003- 2018,
.4.1 3，3.28 ，3.29 |
4.5.2 in GJB 192B- 2011 |
In accordance with GJB 192B-2011
テーブル 6 |
| A divide into groups | solder ability | 3.15 in ZZR-Q / CT 20003- 2018 | 4.4.2 in GJB 192B- 2011 | 13 samples, そして 0 failed |
導入
誘電体とコンデンサの種類
◆高周波タイプ: この種の誘電体材料のコンデンサはクラスⅠコンデンサとみなされます。,
高周波COGを含む、COHコンデンサやHGなどの温度補償用コンデンサ, LG, PH,
rh,SH, TH, UJ, SL. COGの電気的特性、COH コンデンサは最も安定しており、常に変化します。
温度とともに, 電圧と時間. 低損失と高い安定性が要求されるアプリケーションに適しています。,
HG，LG，PH，rh，SH，TH，UJ，SLコンデンサは温度により静電容量が変化します。用途に合わせて選択できます。
低損失および温度補償回路.
◆X7R、X5R、X7S、X6S：X7R、X5R、X7S、X6S材料は誘電率が高い材料の一種です. コンデンサー
この種の材料で作られたコンデンサは、クラスⅠよりも静電容量が大きいクラスⅡコンデンサとみなされます。.
これらのコンデンサは半安定な温度特性を持つものとして分類され、広い温度範囲で使用されます。
範囲, このような種類の回路では, 直流阻止, デカップリング, バイパス, 周波数弁別など.
◆Y5V：この種の材料で作られたコンデンサは、セラミックコンデンサの中で最も高い誘電率を誇ります。. 彼らです
不安定なため、高い静電容量が必要なアプリケーションでは中程度の温度範囲で使用されます。
温度係数, ただし、適度な損失と静電容量の変化が許容できる場合. その静電容量と
散逸率は測定条件に影響されます, 温度や電圧など, 等.
◆Z5U：この種の材料で作られたコンデンサはクラスⅡコンデンサとみなされます。, その温度特性は
X7RとY5Vの間. この種のコンデンサの静電容量は不安定で、温度や温度の影響を受けやすいです。
電圧. 室温に近い環境で低 DC バイアスで動作するアプリケーション回路のバイパスおよびデカップリングに最適.